neutral dry vibrating material for induction furnace
Application Industry: Refractories for Steel Industry
Application Equipment: Induction Furnace Lining (Furnace Lining)
Size: Pre-mixed dry vibrating material with maximum grain size 5 mm (custom formulation on request)
Products Overview
Our Neutral Dry Vibrating Material is a cost-effective dry vibrating material composed of special grade bauxite clinker, corundum, spinel, magnesia, and sintering agent, engineered for steel and alloy melting in induction furnace lining service. The product family delivers high service life and high cost performance, used by many foundry companies with excellent effect.
The Neutral Dry Vibrating Material product family is offered in a single engineering-proven CH-RAM85A chemistry grade (Bauxite-spinel) with alumina content of 72 percent or higher and magnesium content of 18 percent or higher. The CH-RAM85A grade delivers normal use temperature of 1600 to 1650 °C with maximum short-time upper temperature limit of 1700 °C, making it suitable for carbon steel, alloy steel, stainless steel, and high manganese steel smelting.
Sourced from our Xinmi City, Zhengzhou, Henan, China facility, each Neutral Dry Vibrating Material grade is engineered to ASTM, GB/T, and ISO refractory standards. For an overview of the broader catalogue, see the Refractories for the Steel Industry category, or contact our technical sales team for a free consultation against your refractory drawing.
Product Features
Features:
- Manufactured from special grade bauxite clinker, corundum, spinel, magnesia, and sintering agent as the main raw materials
- Engineering-proven cost-effective dry vibrating material for induction furnace lining service
- Suitable for carbon steel, alloy steel, stainless steel, and high manganese steel smelting with high service life
- Used by many foundry companies with excellent effect achieving low cost and long service life
- Single CH-RAM85A chemistry grade with alumina content 72 percent or higher and magnesium content 18 percent or higher
Product Specification
Pre-mixed dry vibrating material is engineered per buyer’s induction furnace lining design. Custom chemistry and grain size optimization available on request.
|
Brands
Items
|
CH-RAM85A Bauxite-spinel |
Typical Value |
|---|---|---|
| Al2O3 content ≥ (%) | 72 | 73.25 |
| MgO content ≥ (%) | 18 | 18.96 |
| Bulk Density ≥ (g/cm³) | 2.8 | 2.83 |
| Normal Service Temperature (°C) | 1600~1650 | 1600~1650 |
| Maximum Service Temperature – Short-term (°C) | 1700 | 1700 |
| Maximum Grain Size (mm) | 5 | 5 |
Note: The product is a single-grade chemistry variant (CH-RAM85A Bauxite-spinel). Typical values shown are representative sample measurements from production. For project-specific chemistry, contact CH Refractories engineering.
Product Applications
Neutral Dry Vibrating Material is a cost-effective dry vibrating material manufactured from special grade bauxite clinker, corundum, spinel, magnesia, and sintering agent, engineered for steel and alloy melting in induction furnace lining service. The product family delivers high service life, high cost performance, and is widely used by foundry companies achieving low cost and long service life in their furnace lining operations.
Application Industry: Refractories for the Steel Industry and the broader Metallurgical Industry.
Target Equipment: Induction Furnace Lining of small, medium-size, and large Induction Furnaces.
Specific Application Zones: The CH-RAM85A Bauxite-spinel grade is optimized for the smelting of carbon steel, alloy steel, stainless steel, and high manganese steel in induction furnace lining service. Normal use temperature range of 1600 to 1650 °C makes the product suitable for medium-temperature induction furnace steel and alloy melting operations. Maximum short-time upper temperature limit of 1700 °C provides safety margin during temperature excursions or transient heating cycles.
CH Refractories is a Neutral Dry Vibrating Material manufacturer in China, Henan, Zhengzhou. The complete Neutral Dry Vibrating Material product family is manufactured in our Xinmi City, Zhengzhou, Henan, China facility to ASTM, GB/T, and ISO refractory standards. Each batch is supported by free consultation, on-site technical support, and a dedicated engineering team serving Refractories for the Steel Industry customers across the global iron and steel value chain.