Burner block for Industrial Furnace

Application Industry: Refractories for Industrial Furnace

Application Equipment: Industrial Furnace Burner Lining

Size: Custom burner block geometry per industrial furnace burner design (free engineering on request)

Consultation：

Products Overview

Our Burner block is a high-performance refractory product engineered for industrial furnace burner lining service. According to the structure and service condition of burner, we successfully developed series of corundum-mullite based and mullite based burner blocks. These products have good properties such as high strength, good thermal resistance, and excellent performance for industrial furnace burner lining service.

The Burner block product family is offered in two engineering-proven SZ chemistry grades. The CH-SZ65 grade features Al₂O₃ content minimum 65% for general industrial furnace burner lining service, with Bulk Density minimum 2.45 g/cm³, Cold Crushing Strength minimum 40 MPa after 110 °C drying for 24 hours and minimum 60 MPa after 1500 °C firing for 3 hours, and Permanent Linear Change maximum 0.5 percent after 1500 °C firing for 3 hours. The CH-SZ75 grade features Al₂O₃ content minimum 75% for higher-demand industrial furnace burner lining service, with Bulk Density minimum 2.6 g/cm³, Cold Crushing Strength minimum 50 MPa after 110 °C drying for 24 hours and minimum 65 MPa after 1500 °C firing for 3 hours, and Permanent Linear Change maximum 0.5 percent after 1500 °C firing for 3 hours.

Sourced from our Xinmi City, Zhengzhou, Henan, China facility, each Burner block grade is engineered to ASTM, GB/T, and ISO refractory standards. For an overview of the broader catalogue, see the Refractories for Industrial Furnace category, or contact our technical sales team for a free consultation against your refractory drawing.

Product Features

Features:

Manufactured from corundum-mullite and mullite based refractory materials as main raw materials
Engineering-proven developed series of corundum-mullite based and mullite based burner blocks with high strength, good thermal resistance, and excellent performance
Two SZ chemistry grades covering Al₂O₃ content 65-75% for matching different industrial furnace burner service requirements
Bulk Density minimum 2.45 to 2.6 g/cm³ and Cold Crushing Strength minimum 40 to 65 MPa depending on grade and curing/firing condition for burner lining service
Designed according to the structure and service condition of burner, suitable for industrial furnace burner lining service with long service life

Product Specification

Burner block

According to the structure and service condition of burner,successfully developed series corundum-mullite based and mullite based burner blocks. These products have good properties such as high strength, good thermal resistance, and excellent performance.

Brands / Items	CH-SZ65	CH-SZ75
Al₂O₃ (%) ≥	65	75
Bulk density (g/cm³) ≥	2.45	2.6
Cold crushing strength (MPa) ≥	40 (110°C, 24h) 60 (1500°C, 3h)	50 (110°C, 24h) 65 (1500°C, 3h)
Permanent linear change (%)	±0.5 (1500°C, 3h)	±0.5 (1500°C, 3h)

Note: Four performance parameters specified per source image: Al₂O₃, Bulk density, Cold crushing strength, and Permanent linear change. Two CH-SZ chemistry grades engineered for industrial furnace burner block service. For project-specific chemistry and grade, contact CH Refractories engineering.

Product Applications

Burner block is a high-performance refractory product engineered for industrial furnace burner lining service. According to the structure and service condition of burner, we successfully developed series of corundum-mullite based and mullite based burner blocks. These products have good properties such as high strength, good thermal resistance, and excellent performance for industrial furnace burner lining service.

Application Industry: Refractories for Industrial Furnace.

Target Equipment: Industrial Furnace Burner Lining of small, medium-size, and large industrial furnace operations.

Specific Application Zones: The CH-SZ65 grade (Al₂O₃ content minimum 65%) is the standard variant for general industrial furnace burner lining service, with Bulk Density minimum 2.45 g/cm³, Cold Crushing Strength minimum 40-60 MPa depending on curing/firing condition, and Permanent Linear Change maximum 0.5 percent after 1500 °C firing for 3 hours. The CH-SZ75 grade (Al₂O₃ content minimum 75%) is the higher-demand variant for industrial furnace burner lining service, with Bulk Density minimum 2.6 g/cm³, Cold Crushing Strength minimum 50-65 MPa depending on curing/firing condition, and Permanent Linear Change maximum 0.5 percent after 1500 °C firing for 3 hours. Both grades are designed according to the structure and service condition of burner, suitable for industrial furnace burner lining service with long service life.

CH Refractories is a Burner block manufacturer in China, Henan, Zhengzhou. The complete Burner block product family is manufactured in our Xinmi City, Zhengzhou, Henan, China facility to ASTM, GB/T, and ISO refractory standards. Each batch is supported by free consultation, on-site technical support, and a dedicated engineering team serving Refractories for Industrial Furnace customers across the global industrial furnace value chain.

Product FAQ

Q1: What is burner block and what are the main applications?

A1: Burner block is a high-performance refractory product engineered for industrial furnace burner lining service. According to the structure and service condition of burner, we successfully developed series of corundum-mullite based and mullite based burner blocks. These products have good properties such as high strength, good thermal resistance, and excellent performance for industrial furnace burner lining service.

Q2: How many chemistry grades of burner block does CH Refractories offer?

A2: CH Refractories offers two engineering-proven SZ chemistry grades of Burner block. The CH-SZ65 grade features Al₂O₃ content minimum 65% for general industrial furnace burner lining service. The CH-SZ75 grade features Al₂O₃ content minimum 75% for higher-demand industrial furnace burner lining service. Both grades are designed according to the structure and service condition of burner for industrial furnace burner lining service with high strength, good thermal resistance, and excellent performance.

Q3: What are the test conditions for burner block?

A3: Burner block delivers Bulk Density minimum 2.45 to 2.6 g/cm³ depending on grade. Cold Crushing Strength is minimum 40 to 65 MPa depending on grade and curing/firing condition (110 °C × 24h and 1500 °C × 3h). Permanent Linear Change is maximum 0.5 percent after 1500 °C firing for 3 hours for both grades. The burner block product family has high strength, good thermal resistance, and excellent performance for industrial furnace burner lining service.

Q4: Can the burner block be customized to specific industrial furnace burner designs?

A4: Yes. CH Refractories offers custom chemistry, grade, and geometry optimization against the buyer's specific industrial furnace burner lining design and operating conditions. CH Refractories engineers can adjust Al₂O₃ content, raw material formulation, and geometry design to meet specific industrial furnace burner service temperature and operating conditions. Please send the industrial furnace burner drawing, lining design, furnace capacity, and operating temperature data to our engineering team in Xinmi City, Zhengzhou, Henan, China for a free consultation, on-site technical support, and a tailored burner block formulation proposal with optimized grade selection, raw material adjustment, and geometry design for your specific industrial furnace burner service conditions.