Fused AZS ramming mass
Application Industry: Refractories for Glass Industry
Application Equipment: Glass Furnace Sealing Layer and Frit Bath Kiln Pool
Size: Custom fused AZS ramming mass geometry per glass furnace and frit bath kiln design (free engineering on request)
Products Overview
Our Fused AZS ramming mass is a high-performance unshaped refractory product engineered for glass furnace sealing layer and frit bath kiln pool service. The zircon ramming material is an unshaped refractory material with strong fluidity and easy operation. It is composed of molten corundum aggregate particles and a small amount of additives. The product has the characteristics of convenient use, hardening at room temperature, high compressive strength in high temperature, small thermal expansion and shrinkage, and strong resistance to solution corrosion. It is the most ideal indeterminate refractory material used in the sealing layer of glass and frit bath kiln.
The Fused AZS ramming mass product family is offered in one engineering-proven chemistry grade, the Fused AZS ramming mass grade. The grade features ZrO2 content minimum 28% for glass furnace and frit bath kiln sealing layer service, with Bulk Density minimum 2.9 g/cm3, Normal Temperature Compressive Strength minimum 50 MPa after 110 °C drying, Refractoriness minimum 1770 °C, Maximum Service Temperature 1650 °C, and Use Density 3000 kg/m3. The product family has the characteristics of convenient use, hardening at room temperature, high compressive strength in high temperature, small thermal expansion and shrinkage, and strong resistance to solution corrosion for glass furnace and frit bath kiln sealing layer service.
Sourced from our Xinmi City, Zhengzhou, Henan, China facility, the Fused AZS ramming mass product family is engineered to ASTM, GB/T, and ISO refractory standards. For an overview of the broader catalogue, see the Refractories for Glass Industry category, or contact our technical sales team for a free consultation against your refractory drawing.
Product Features
Our Fused AZS ramming mass is a high-performance unshaped refractory product engineered for glass furnace sealing layer and frit bath kiln pool service. The zircon ramming material is an unshaped refractory material with strong fluidity and easy operation. It is composed of molten corundum aggregate particles and a small amount of additives. The product has the characteristics of convenient use, hardening at room temperature, high compressive strength in high temperature, small thermal expansion and shrinkage, and strong resistance to solution corrosion. It is the most ideal indeterminate refractory material used in the sealing layer of glass and frit bath kiln.
The Fused AZS ramming mass product family is offered in one engineering-proven chemistry grade, the Fused AZS ramming mass grade. The grade features ZrO2 content minimum 28% for glass furnace and frit bath kiln sealing layer service, with Bulk Density minimum 2.9 g/cm3, Normal Temperature Compressive Strength minimum 50 MPa after 110 °C drying, Refractoriness minimum 1770 °C, Maximum Service Temperature 1650 °C, and Use Density 3000 kg/m3. The product family has the characteristics of convenient use, hardening at room temperature, high compressive strength in high temperature, small thermal expansion and shrinkage, and strong resistance to solution corrosion for glass furnace and frit bath kiln sealing layer service.
Sourced from our Xinmi City, Zhengzhou, Henan, China facility, the Fused AZS ramming mass product family is engineered to ASTM, GB/T, and ISO refractory standards. For an overview of the broader catalogue, see the Refractories for Glass Industry category, or contact our technical sales team for a free consultation against your refractory drawing.
Product Specification
Zirconium ramming mass is an unshaped refractory material with strong fluidity and easy operation. It is composed of molten corundum aggregate particles and a small amount of additives. The product has the characteristics of convenient use, hardening at room temperature, high compressive strength in high temperature, small thermal expansion and shrinkage, and strong resistance to solution corrosion. It is the most ideal indeterminate refractory material used in the sealing layer of glass and frit bath kiln.
Zirconium ramming material is prepared by using high-quality zirconium aggregate, powder material, aluminum phosphate as binder and admixture, which has low thermal conductivity, good thermal shock resistance, chemical stability and melting. Glass and liquid metal have good corrosion resistance, work stability under oxidizing atmosphere, and do not chemically react with molten metal. It is an excellent thermosetting amorphous refractory material. Widely used in the field of glass furnace kiln, ladle and circulating fluidized bed boiler.
| Brands / Items | Fused AZS ramming mass |
|---|---|
| ZrO2 (%) ≥ | 28 |
| Bulk density BD (g/cm³) ≥ | 2.9 |
| Normal temperature compressive strength CCS (MPa) ≥ (110°C Drying) |
50 |
| Refractoriness (°C) ≥ | 1770 |
| Max appl. temp (°C) | 1650 |
| Use density (kg/m³) | 3000 |
Note: Six performance parameters specified per source image: ZrO2 content, Bulk density, Normal temperature compressive strength, Refractoriness, Max appl. temp, and Use density. One Fused AZS ramming mass chemistry grade engineered for glass furnace kiln sealing layer, ladle, and circulating fluidized bed boiler service. For project-specific chemistry and geometry, contact CH Refractories engineering.
Product Applications
Fused AZS ramming mass is a high-performance unshaped refractory product engineered for glass furnace sealing layer and frit bath kiln pool service. The zircon ramming material is an unshaped refractory material with strong fluidity and easy operation. It is composed of molten corundum aggregate particles and a small amount of additives. The product has the characteristics of convenient use, hardening at room temperature, high compressive strength in high temperature, small thermal expansion and shrinkage, and strong resistance to solution corrosion. It is the most ideal indeterminate refractory material used in the sealing layer of glass and frit bath kiln.
Application Industry: Refractories for Glass Industry.
Target Equipment: Glass Furnace Sealing Layer and Frit Bath Kiln Pool of small, medium-size, and large glass industrial operations.
Specific Application Zones: The Fused AZS ramming mass grade is engineered for glass furnace sealing layer and frit bath kiln pool service. The grade delivers ZrO2 content minimum 28%, Bulk Density minimum 2.9 g/cm3, Normal Temperature Compressive Strength minimum 50 MPa after 110 °C drying, Refractoriness minimum 1770 °C, Maximum Service Temperature 1650 °C, and Use Density 3000 kg/m3. The product family has the characteristics of convenient use, hardening at room temperature, high compressive strength in high temperature, small thermal expansion and shrinkage, and strong resistance to solution corrosion for glass furnace and frit bath kiln sealing layer service.
CH Refractories is a Fused AZS ramming mass manufacturer in China, Henan, Zhengzhou. The complete Fused AZS ramming mass product family is manufactured in our Xinmi City, Zhengzhou, Henan, China facility to ASTM, GB/T, and ISO refractory standards. Each batch is supported by free consultation, on-site technical support, and a dedicated engineering team serving Refractories for Glass Industry customers across the global glass value chain.